Ink on a 5.5 by 9 inch substrate of 60-pound offset matte white paper. Composed of: varnish (soy bean oil [C57H98O6], used as a plasticizer: 52%. Phenolic modified rosin resin [Tall oil rosin: 66.2%. Nonylphenol [C15H24O]: 16.6%. Formaldehyde [CH2O]: 4.8%. Maleic anhydride [C4H2O3]: 2.6%. Glycerol [C3H8O3]: 9.6%. Traces of alkali catalyst:.2%]: 47%): 53.7%. 100S Type Alkyd used as a binder (Reaction product of linseed oil: 50.7%. Isophthalic acid [C8H6O4]: 9.5%. Trimethylolpropane [CH3CH2C(CH2OH)3]: 4.7%. Reaction product of tall oil rosin: 12.5%. Maleic anhydride [C4H2O3]: 2.5%. Pentaerythritol [C5H12O4]: 5%. Aliphatic C14 Hydrocarbon: 15%): 19.4%. Carbon Black (C: 92.8%. Petroleum: 5.1%. With sulfur, chlorine, and oxygen contaminates: 2.1%), used as a pigmenting agent: 18.6%. Tung oil (Eleostearic acid [C18H30O2]: 81.9%. Linoleic acid [C18H32O2]: 8.2%. Palmitic acid [C16H32O2]: 5.9%. Oleic acid [CH3(CH2)7CH=CH(CH2)7COOH]: 4.0%.), used as a reducer: 3.3%. Micronized polyethylene wax (C2H4) N: 2.8%. 3/50 Manganese compound, used as a through drier: 1.3%. 1/25 Cobalt linoleate compound used as a top drier:.7%. Residues of blanket wash (roughly equal parts aliphatic hydrocarbon and aromatic hydrocarbon):.2%. Adhered to: cellulose [C6H10O5] from softwood sulphite pulp (Pozone Process) of White Spruce (65%) and Jack Pine (35%): 77%; hardwood pulp (enzyme process pre-bleach Kraft pulp) of White Poplar (aspen): 15%; and batch treated PCW (8%): 69.3%. Water [H2O]: 11.0%. Clay [Kaolinite form aluminum silicate hydroxide (Al2Si2O5[OH]4): 86%. Calcium carbonate (CaCO3): 12%. Diethylenetriamine: 2%], used as a pigmenting filler: 8.4%. Hydrogen peroxide [H2O2], used as a brightening agent: 3.6%. Rosin soap, used as a sizer: 2.7%. Aluminum sulfate [Al2(SO4)]: 1.8%. Residues of cationic softener (H2O: 83.8%. Base [Stearic acid (C18H36O2): 53.8%. Palmitic acid (C16H32O2): 29%. Aminoethylethanolamine (H2-NC2-H4-NHC2-H4-OH): 17.2%]: 10.8%. Sucroseoxyacetate: 4.9%. Tallow Amine, used as a surfactant: 0.3%. Sodium chloride [NaCl], used as a viscosity controlling agent:.2%) and non-ionic emulsifying defoamer (sodium salt of dioctylsulphosuccinate [C20H37NaO7S]), combined: 1.7%. Miscellaneous foreign contaminates: 1.5%.